ET01B NiCr  Alloy for fixed metal-to-ceramic with Beryllium

 Description:

Ni:79%
Cr:13%
MO:5%
Be:1.7%
Melting range: 1240°C~ 1290°C
Yield strength: 560 Mpa
Elongation: 12%
Density: 8.1/cm2
Coefficient of liner expansion:13.8x10*K"(25 to 500°C)

Shape：VB
Diameter:12.5mm  Height：4mm
Diameter:12.5mm  Height：7mm

ET03B NiCr Alloy for Framework and Partial with Beryllium

Description:

Ni:72%
Cr:14%
Mo:6%
Be:1.8%
Melting range: 1240°C~1280°C
Yield strength: 520MPa
Elongation:6%
Elastic Modulus: 200Gpa
Vickers hardness: 360HV10

Size:Diameter 14mm, height 10mm