    NiCr Alloy for fixed metal-to-ceramic Beryllium-free

     

    ET01 NiCr Alloy for fixed metal-to-ceramic Beryllium-free

    High bio-safe dental casting alloy, beryllium free, it has perfect ductility and toughness, excellent casting property and high corrosion-resistant.

    Technical Data & Composition

    Ni:62%
    Cr:24%
    MO:9.8%
    A1:1.3%
    Ne:1.3%
    Si:1.2%

    Density:8.2 (g/cm3)
    Hardness:210 HV10
    Melting Range:1300°C-1340°C
    Yield Strength:≥250 MPa
    Elongation:≥3.0%
    Coefficient of Liner Expansion (25-500°C):14.5X 10-6K-1

    Size:Diameter 8mm, height 15mm

    ET03 Co-Base Dental Alloy

     

     
     - ET02
    ET02

    CoCr Alloy for fixed metal-to-ceramic Beryllium-free

     

    ET02 CoCr  Alloy for fixed metal-to-ceramic Beryllium-free

    Description:
    Available forms: columnar ingot
    Compositions:

    Co:62.0%
    Cr:25.0%
    Mo:6.0%
    W:5%
    Nb:1.0%
    Si:1.0%

    Density: 8.2g/cm³

    Melting range: 1320°C~1370°c

    Vickers hardness: 210HV10

    Elongation: 12%
    Yield Strength After Casting: ≥250Mpa
    Coefficient of liner expansion: 14.5×10K(25 to 500°C)

    Size:Diameter 8mm, height 15mm
    ET02 Co-Base Dental Alloy

     
     - ET03
    ET03

    CoCr Dental Alloy for Framework and Partial Beryllium-free

     

    ET03 CoCr Dental Alloy for Framework and Partial Beryllium-free

     Description:
    Available forms: columnar ingot
    Compositions:

    Co:62%
    Cr: 27%
    Mo:6%
    Fe:2.5%
    Si:1.3%
    and the rest

    Melting range: 1350°C~1370°c

    Yield strength: 520MPa
    Elongation:2%
    Elastic Modulus: 210Gpa

    Vickers hardness: 360HV10

    Size:Diameter 8mm, height 17mm

    SDT-ET03 Co-Base Dental Alloy